Volkswagen Tiguan Service and Repair Manual: Two-Part HS Premium Filler

Definition:

  • Two-Part HS Premium Filler -LVM 013 171 A4-, dark gray
  • Two-Part HS Premium Filler -LGF 013 007 A4-, light gray
  • Two-Part HS Premium Filler -LGF 013 100 A4-, white
  • Two-Part HS Premium Filler -LGF 013 190 A4-, anthracite

Product Description

These two-part premium fillers are high-quality two-part HS acrylic-resin-based fillers.

Properties:

  • Very long processing time
  • Optimal and stable processing properties
  • Sands well
  • Great stability under load
  • High yield
  • Excellent high-build characteristics
  • Excellent paint finish

Application Instructions

Base Surface

Suitable base surfaces:

  • sheet steel that has been cleaned, sanded and primed with Two-Part Wash Primer -LHV 043 000 A2- or One-Part Wash Primer -LVM 044 007/171 A2-, galvanized/electrolytically zinced sheet steel or soft aluminum
  • Fine or non-sanded, thoroughly cleaned, original factory primer.
  • Sanded factory paint or old paint (including thermoplastic coatings)
  • Surfaces prepared with two-part polyester products and then sanded very fine.
  • Cleaned and sanded UP-GF surfaces, free of separating agents

Pre-treatment of base surfaces:

  • Carefully clean using Silicone Remover -LVM 020 000 A5- or Silicone Remover, Long -LVM 020 100 A5-.

Volswagen Tiguan. P00-10038

  • Then, sand.

Volswagen Tiguan. P00-10037

  • Use a suitable cleaning agent before reworking to ensure a clean and residue-free surface.

Volswagen Tiguan. P00-10038

Processing

Mixture ratio:

4:1 by volume with:

  • Two-Part HS Hardener -LHA 009 041 A3-
  • Two-Part HS Hardener, Short -LHA 021 004 A3-
  • Two-Part HS Hardener, Extra Short -LHA 009 046 A2-
  • Two-Part HS Hardener, Long -LHA 009 047 A3-
  • Two-Part HS Hardener, Extra Long -LHA 009 048 A3-

Volswagen Tiguan. P00-10024

Mixture ratio:

7:1 by volume with:

  • Two-Part VHS Hardener, Short -LHA 009 050 A2-
  • Two-Part VHS Hardener -LHA 009 051 A2-/-LVM 009 051 A5-
  • Two-Part VHS Hardener, Long -LHA 009 052 A2-/-LHA 009 052 A3-
  • Two-Part VHS Hardener, Extra Long -LHA 009 053 A2-

Volswagen Tiguan. P00-10024

For elastification. Refer to → Anchor.

Processing time/pot life:

  • Ready to spray 90 to 120 minutes at +20 ºC (68 ºF) (depending on the hardener used).

Thinner:

  • Two-Part Thinner -LVE 009 001 A5-
  • Two-Part Thinner, Long -LVM 009 300 A2-
  • Two-Part Thinner, Plus -LHA 014 000 A5-
  • Two-Part Thinner, Special -LVM 009 200 A2/A5-

Volswagen Tiguan. P00-10029

Application type "coat"

Volswagen Tiguan. P00-10032

  • Processing viscosity 4 mm for +20 ºC (68 ºF), German Industry Standardization 53211

Processing viscosity 4 mm gravity feed spraygun "Compliant" and "HVLP" is the mixed viscosity.

Volswagen Tiguan. P00-10036

Adding 10 % VHS hardener at +20 ºC (68 ºF) material temperature

Adding HS hardener is not required, but up to 10 % is possible.

  • Use a measuring stick to mix when pouring in the hardener.

Volswagen Tiguan. P00-10023

  • Set spray nozzle (see manufacturer's information): "Compliant" 1.6 to 1.8 mm.
  • Set spray nozzle (see manufacturer's information): "HVLP" 1.5 to 1.9 mm.
  • Set spray pressure (see manufacturer's information): "Compliant" to 1.5 to 3.0 bar.
  • Set atomizing pressure (see manufacturer's information): "HVLP" 0.7 bar.
  • Three spray applications are required to get a dry layer thickness of between 80 and 300 um.

Volswagen Tiguan. P00-10029

When air drying, the maximum dry layer thickness is 300 um.

When forced drying, the maximum dry layer thickness is 250 um.

When IR drying (white and light gray), the maximum dry layer thickness is 200 um.

When IR drying (black), the maximum dry layer thickness is 180 um.

The recommended dry layer thickness is between 80 and 200 um.

Volswagen Tiguan. P00-10032

Drying

The material can be sanded after 3 to 4 hours (layer thickness of 80 to 150 um after air drying at +20 ºC (68 ºF) room temperature).

If the applied layer thickness is between 150 and 300 um, the material should be allowed to dry over night and then sanded.

Volswagen Tiguan. P00-10027

Final drying time with forced drying is a minimum of 5 to 15 minutes.

Volswagen Tiguan. P00-10026

Forced drying at +60 ºC (140 ºF) object temperature for 25 to 30 minutes for a layer thickness of between 80 and 150 um; 35 to 45 minutes for a layer thickness of between 150 and 250 um

Volswagen Tiguan. P00-10027

Final drying time for IR drying is a minimum of 5 to 15 minutes.

Volswagen Tiguan. P00-10026

IR drying (depending on layer thickness) with medium-wave heater for 15 to 20 minutes and short-wave heater for 10 to 15 minutes

Volswagen Tiguan. P00-10028

Further Processing

  • Dry-sand with rotary sander and dust extraction. P400-500 grit sandpaper

Volswagen Tiguan. P00-10040

  • Wet-sand with P800-1000 grit sandpaper

Volswagen Tiguan. P00-10041

Reworking

Can be painted over with:

  • Water-based base paint and two-part HS clear coat
  • Two-Part HS Top Coat

Special Instructions

Elastification for rigid and semi-rigid plastics:

  • The base material must first be mixed with 15 % Elastic Additive -ALZ 011 001-. 3:1 mixing ratio for HS hardener without thinner, 4:1 mixing ratio for VHS hardener with 5 % thinner.
  • Any faults in the base surface can be filled with two-part polyester filling paste. After drying and intermediate sanding, insulate the filler patches with two-part HS premium filler.
  • The best insulating effect, even with critical surfaces, is achieved with a medium layer of 80 to 120 um in 2 spray passes, with air-drying overnight, or oven or IR drying. With critical surfaces, fine preparation is required and the parts must be evenly filled.
  • The Two-Part HS Vario Filler -LGF 786 004 A4- (gray) is recommended for insulating thermoplastic coatings.

Volswagen Tiguan. P00-10029

Personal Protective Equipment:

  • Note the safety data sheets
  • Wear the personal protective equipment during application

Volswagen Tiguan. P00-10820

Characteristics

Delivery Viscosity Thixotropic
Flashpoint: above 23 ºC (73.4 ºF)
VOC value: 2004/42/IIB(c)(540)540 The EU limit for this product (product category IIB.b) in ready-to-use form is a maximum of 540 g/L volatile organic compounds. The VOC value of this product in ready-to-use form is a maximum of 540 g/L.

Storage

The guaranteed shelf life is 24 months from production date. Use no later than the date indicated on the label and store in original container at +20 ºC (68 ºF).

Volswagen Tiguan. P00-10050

    Two-Part HS Vario Filler
    Definition: Two-Part HS Vario Filler -LGF 786 004 A4-, gray Product Description The two-part vario filler is a high-quality, variable VOC compliant, acrylic-based two-part HS filler. Properties: ...

    Two-Part HS Mixed Filler
    Definition: Two-Part HS Mixed Filler -LGF 810 150 A4-, white Two-Part HS Mixed Filler -LGF 810 151 A4-, black Two-Part HS Mixed Filler -LGF 810 152 A4-, red Two-Part HS Mixed Filler -LGF 810 153 ...

    See More:

    Volkswagen Tiguan Service and Repair Manual > General Application Instructions for Repair and Painting Systems: Paint System for Plastic Parts
    This universal painting system enables you to safely and simply paint all plastic parts which can be usually found on the exterior. (Plastic types: PP, EPDM, ABS, PC, PPO, PBTP, UP-GF, PA, PVC, R-TPU, PUR) This technical reference material does not apply to factory primed plastic parts. Base Surf ...

    Volkswagen Tiguan Owners Manual

    Volkswagen Tiguan Service and Repair Manual

    © 2018-2021 Copyright www.vwtiguan.org - 0.0144